This work introduces a method for co-localized multi-modal imaging of sub-μm features in an additively manufactured (AM) titanium alloy. Ti-6Al-4V parts manufactured by electron beam melting powder bed fusion were subjected to hot isostatic pressing to seal internal porosity and machined to remove contour–hatch interfaces. Electron microscopy and atomic force microscopy-based techniques (electron backscatter diffraction and scanning Kelvin probe force microscopy) were used to measure and categorize the effects of crystallographic texture, misorientation, and phase content on the relative differences in the Volta potential of α-Ti and β-Ti phases. Given the tunability of additive manufacturing processes, recommendations for texture and phase control are discussed. In particular, our findings indicate that the potential for micro-galvanic corrosion initiation can be regulated in AM Ti-6Al-4V parts by minimizing both the total area of {111} prior-β grains and the number of contact points between {111} β grains and α laths that originate from {001} prior-β grains. 

Abstract Thermoelectric generators are an environmentally friendly and reliable solid‐state energy conversion technology. Flexible and low‐cost thermoelectric generators are especially suited to power flexible electronics and sensors using body heat or other ambient heat sources. Bismuth telluride (Bi₂Te₃) based thermoelectric materials exhibit their best performance near room temperature making them an ideal candidate to power wearable electronics and sensors using body heat. In this report, Bi₂Te₃thin films are deposited on a flexible polyimide substrate using low‐cost and scalable manufacturing methods. The synthesized Bi₂Te₃nanocrystals have a thickness of 35 ± 15 nm and a lateral dimension of 692 ± 186 nm. Thin films fabricated from these nanocrystals exhibit a peak power factor of 0.35 mW m⁻¹·K⁻²at 433 K, which is among the highest reported values for flexible thermoelectric films. In order to evaluate the flexibility of the thin films, static and dynamic bending tests are performed while monitoring the change in electrical resistivity. After 1000 bending cycles over a 50 mm radius of curvature, the change in electrical resistance of the film is 23%. Using Bi₂Te₃solutions, the ability to print thermoelectric thin films with an aerosol jet printer is demonstrated, highlighting the potential of additive manufacturing techniques for fabricating flexible thermoelectric generators.